Structures Formation on the Y-TZP-AI[2]O[3] Ceramic Composites Surface / S. N. Kulkov [et al.]
Уровень набора: (RuTPU)RU\TPU\network\2008, IOP Conference Series: Materials Science and EngineeringЯзык: английский.Страна: .Резюме или реферат: The paper discusses the structure of Y-TZP-Al[2]O[3] ceramics produced from nanopowders and friction surface, wear resistance, friction coefficient of Y-TZP-AEO[3] composites rubbed against a steel disk counterface at a pressure of 5 MPa in a range of sliding speeds from 0.2 to 47 m/s. Analysis by X-ray diffraction, scanning electron microscopy showed that the high wear resistance of Y-TZP-Al[2]O[3] composites at high sliding speeds is due to high-temperature phase transitions and protective film formation on the friction surface..Примечания о наличии в документе библиографии/указателя: [References: 6 tit.].Тематика: электронный ресурс | труды учёных ТПУ | керамические композиты | поверхности | нанопорошки | рентгеновская дифракция | износостойкость | композиты | защитные пленки | трение Ресурсы он-лайн:Щелкните здесь для доступа в онлайн | Щелкните здесь для доступа в онлайнНет реальных экземпляров для этой записи
Title screen
[References: 6 tit.]
The paper discusses the structure of Y-TZP-Al[2]O[3] ceramics produced from nanopowders and friction surface, wear resistance, friction coefficient of Y-TZP-AEO[3] composites rubbed against a steel disk counterface at a pressure of 5 MPa in a range of sliding speeds from 0.2 to 47 m/s. Analysis by X-ray diffraction, scanning electron microscopy showed that the high wear resistance of Y-TZP-Al[2]O[3] composites at high sliding speeds is due to high-temperature phase transitions and protective film formation on the friction surface.
Для данного заглавия нет комментариев.
Личный кабинет оставить комментарий.