Evolution of the Curvature and Torsion of a Crystal Lattice upon Deformation in Different Substructures of Copper-Based Alloys / N. A. Koneva, L. I. Trishkina, T. V. Cherkasova
Уровень набора: Bulletin of the Russian Academy of Sciences: Physics, Scientific Journal = 2007-Язык: английский.Резюме или реферат: The results are presented from an electron microscopic study of the curvature/torsion (χ) of the crystal lattice that occurs upon the deformation of polycrystalline solid FCC solutions. Alloys Cu + 0.4 at % Mn and Cu + 19 at % Mn with mean grain size 〈d〉 = 10-240 μm are investigated. Samples are deformed by tension at room temperature. Causes of curvature/torsion found. It is found that the highest values of χ are characteristic of the joints of grains and grain boundaries..Примечания о наличии в документе библиографии/указателя: [References: p. 759 (15 tit.)].Аудитория: .Тематика: электронный ресурс | труды учёных ТПУ | кристаллическая решетка | деформация | сплавы Ресурсы он-лайн:Щелкните здесь для доступа в онлайнНет реальных экземпляров для этой записи
Title screen
[References: p. 759 (15 tit.)]
The results are presented from an electron microscopic study of the curvature/torsion (χ) of the crystal lattice that occurs upon the deformation of polycrystalline solid FCC solutions. Alloys Cu + 0.4 at % Mn and Cu + 19 at % Mn with mean grain size 〈d〉 = 10-240 μm are investigated. Samples are deformed by tension at room temperature. Causes of curvature/torsion found. It is found that the highest values of χ are characteristic of the joints of grains and grain boundaries.
Для данного заглавия нет комментариев.
Личный кабинет оставить комментарий.