Change of the spring Сr-Ni alloy microstructure after ageing [Electronic resource] / M. K. Skakov [et al.]
Уровень набора: (RuTPU)RU\TPU\book\169973, Bulletin of the Tomsk Polytechnic University / Tomsk Polytechnic University (TPU) = 2006-2007Язык: английский ; оригинала, русский.Страна: Россия.Описание: 1 файл (1.1 Мб)Серия: Mathematics and mechanics.PhysicsРезюме или реферат: It has been stated that ageing of the tempered alloy 47ХНМ at temperature 500 °С during 5...10 h does not result in disintegration of oversaturated firm solution, at ageing temperature rise up to 600 °C attributes of disintegration in particles of α-phase of homogeneoustype start to be shown. It was shown that after tempered samples ageing at 700 °C the faltering disintegration with allocation of not coherent α-phase on the basis of chrome develops intensively, and its volume fraction increases with increase in ageing time reaching the maximal values in 5...10 h of ageing.Примечания о наличии в документе библиографии/указателя: [Bibliography: p. 113 (5 titles)].Тематика: microstructures | spring alloys | ageing | temperature | disintegration | oversaturated firm solution | particles | homogeneoustype | samples | chrome | электронный ресурс Ресурсы он-лайн:Щелкните здесь для доступа в онлайнЗаглавие с титульного листа
Электронная версия печатной публикации
[Bibliography: p. 113 (5 titles)]
It has been stated that ageing of the tempered alloy 47ХНМ at temperature 500 °С during 5...10 h does not result in disintegration of oversaturated firm solution, at ageing temperature rise up to 600 °C attributes of disintegration in particles of α-phase of homogeneoustype start to be shown. It was shown that after tempered samples ageing at 700 °C the faltering disintegration with allocation of not coherent α-phase on the basis of chrome develops intensively, and its volume fraction increases with increase in ageing time reaching the maximal values in 5...10 h of ageing
Adobe Reader
Для данного заглавия нет комментариев.