A composite explosive emission cathode made from a metal ceramic with lanthanum and titanium borides / V. I. Boyko (Boiko), O. Yu. Dolmatov, B. E. Kadlubovich

Уровень набора: Instruments and Experimental Techniques, journal = 1958-Основной Автор-лицо: Boyko (Boiko), V. I., Doctor of Physical and Mathematical Sciences, Professor of the TPU, 1943-, Vladimir IlyichАльтернативный автор-лицо: Dolmatov, O. Yu., Physicist, Associate Professor of Tomsk Polytechnic University, Candidate of physical and mathematical sciences, 1967-, Oleg Yurevich;Kadlubovich, B. E.Язык: английский.Страна: Россия.Резюме или реферат: A composite explosive emission cathode for generating large-diameter electron beams has been fabricated form LaB6-TiB2 produced by self-sustaining high-temperature synthesis. Electron microscope studies of the emitting surface indicate that the height of micropoints is 2-13 μm, their base diameters are 5-13 μm, and their density is 2.106 cm-2. Cathode emission characteristics measured at the OMEGA-350 accelerator are compared to those of a steel emitter..Аудитория: .Тематика: труды учёных ТПУ
Тэги из этой библиотеки: Нет тэгов из этой библиотеки для этого заглавия. Авторизуйтесь, чтобы добавить теги.
Оценка
    Средний рейтинг: 0.0 (0 голосов)
Нет реальных экземпляров для этой записи

A composite explosive emission cathode for generating large-diameter electron beams has been fabricated form LaB6-TiB2 produced by self-sustaining high-temperature synthesis. Electron microscope studies of the emitting surface indicate that the height of micropoints is 2-13 μm, their base diameters are 5-13 μm, and their density is 2.106 cm-2. Cathode emission characteristics measured at the OMEGA-350 accelerator are compared to those of a steel emitter.

Для данного заглавия нет комментариев.

оставить комментарий.