Thermal analysis of copper-containing oxide systems produced by AC electrochemical oxidation of metals / N. V. Usoltseva, A. S. Dolinina, I. V. Frolova = Термический анализ медьсодержащих оксидных систем, полученных электрохимическим окислением металлов
Уровень набора: International Conference on Thermal Analysis and Calorimetry in Russia (RTAC-2016), 16-23 September, 2016 Saint-Petersburg, Russia : proceeding = 2016Язык: русский ; резюме, eng.Страна: Россия.Серия: Section 1: Thermal analysis and calorimetry of inorganic substances and materialsРезюме или реферат: The products of AC electrochemical oxidation of metals were characterized by DSC/DTG analysis. Individual copper oxidation and joint oxidation of copper and aluminum / cadmium was carried out in sodium chloride. Copper oxide (I) which is formed by AC copper oxidation is oxidized to copper oxide (II) at 260 °C. The product of joint oxidation of copper and aluminum consists of copper oxide (I) and aluminum oxyhydroxide (Cu2O, AlOOH). At joint oxidation of copper and cadmium the oxides and hydroxides of copper and cadmium (γ-Cd(OH)2, Cu(OH)2, β-Cd(OH)2, CdO and Cu2O) are formed. Joint AC oxidation with aluminium does not affect the temperature of Cu2O oxidation whereas electrolysis with cadmium causes the temperature increate to 320°C.; ДСК/ДТГ анализ использовался для установления температур фазовых превращений в продуктах электрохимического окисления металлов на переменном токе. Индивидуальное окисление меди и совместное окисление меди и алюминия / кадмия проводилось в растворе хлорида натрия. Оксид меди (I), образующийся при переменнотоковом электрохимическом окислении меди, окисляется до оксида меди (II) при 260°С. Продукт совместного окисления меди и алюминия состоит из оксида меди (I) и оксигидроксида алюминия (Cu2O, AlOOH), а при совместном окислении меди и кадмия образуются оксиды и гидроксиды меди и кадмия: γ-Cd(OH)2, Cu(OH)2, β-Cd(OH)2, CdO и Cu2O. Проведение электролиза с алюминием не влияет на температуру окисления Cu2O, а с кадмием - повышает температуру до 320°С..Примечания о наличии в документе библиографии/указателя: References: p. 458 (6 tit).Аудитория: .Тематика: труды учёных ТПУ | термический анализ | оксидные системы | электрохимическое окисление | металлыReferences: p. 458 (6 tit)
The products of AC electrochemical oxidation of metals were characterized by DSC/DTG analysis. Individual copper oxidation and joint oxidation of copper and aluminum / cadmium was carried out in sodium chloride. Copper oxide (I) which is formed by AC copper oxidation is oxidized to copper oxide (II) at 260 °C. The product of joint oxidation of copper and aluminum consists of copper oxide (I) and aluminum oxyhydroxide (Cu2O, AlOOH). At joint oxidation of copper and cadmium the oxides and hydroxides of copper and cadmium (γ-Cd(OH)2, Cu(OH)2, β-Cd(OH)2, CdO and Cu2O) are formed. Joint AC oxidation with aluminium does not affect the temperature of Cu2O oxidation whereas electrolysis with cadmium causes the temperature increate to 320°C.
ДСК/ДТГ анализ использовался для установления температур фазовых превращений в продуктах электрохимического окисления металлов на переменном токе. Индивидуальное окисление меди и совместное окисление меди и алюминия / кадмия проводилось в растворе хлорида натрия. Оксид меди (I), образующийся при переменнотоковом электрохимическом окислении меди, окисляется до оксида меди (II) при 260°С. Продукт совместного окисления меди и алюминия состоит из оксида меди (I) и оксигидроксида алюминия (Cu2O, AlOOH), а при совместном окислении меди и кадмия образуются оксиды и гидроксиды меди и кадмия: γ-Cd(OH)2, Cu(OH)2, β-Cd(OH)2, CdO и Cu2O. Проведение электролиза с алюминием не влияет на температуру окисления Cu2O, а с кадмием - повышает температуру до 320°С.
Для данного заглавия нет комментариев.