Friction and the development of hard alloy surface microstructures during wear / S. F. Gnyusov, S. Yu. Tarasov
Уровень набора: Journal of Materials Engineering and Performance, Scientific JournalЯзык: английский.Страна: .Резюме или реферат: Investigations of wear in sliding friction of WC-Hadfield steel hard alloy against cast tool steel have been carried out in a broad range of velocities and pressure values. Structural and phase composition variations have been revealed. Friction-affected zone was found to be 450 µm in depth. Structural a, transformation regions are located within 100 µm of the surface. These transformations contributed to the total solid solution deformation hardening.Примечания о наличии в документе библиографии/указателя: [References: p. 742 (2 tit.)].Аудитория: .Тематика: электронный ресурс | труды учёных ТПУ | трансформации трения | WC-Co | WC-Ni Ресурсы он-лайн:Щелкните здесь для доступа в онлайнНет реальных экземпляров для этой записи
Title screen
[References: p. 742 (2 tit.)]
Investigations of wear in sliding friction of WC-Hadfield steel hard alloy against cast tool steel have been carried out in a broad range of velocities and pressure values. Structural and phase composition variations have been revealed. Friction-affected zone was found to be 450 µm in depth. Structural a, transformation regions are located within 100 µm of the surface. These transformations contributed to the total solid solution deformation hardening
Для данного заглавия нет комментариев.
Личный кабинет оставить комментарий.