Thermal Processes and Peculiarities of Multilayer Coating Structure based on Cr20Ag20 Obtained by Electronic Radial Deposition / N. A. Narkevich, E. A. Ivanova, V. V. Kibitkin
Язык: английский.Страна: Россия.Резюме или реферат: In the work composition material has been investigated based on steel Cr20NMn20 deposited for several passes until obtaining the layer 6 mm for steel base 3, of dimensions 120x20 mm and thickness 3 mm at the installation ERI-5. Selection of coating composition is conditioned by prospect of its application as the material possessing high wear-resistant properties under the conditions of abrasive wear and contact friction with high specific loads. Coating structure has been investigated through metallographic microscope of the instrument NANOHARDNESS TESTER. Estimation of thermal processes in the zone of electronic beam in mutual relations with experimental investigation of the structure and phase composition of coating is thus investigated..Примечания о наличии в документе библиографии/указателя: [References: p. 140 (4 tit.)].Аудитория: .Тематика: электронный ресурс | труды учёных ТПУ Ресурсы он-лайн:Щелкните здесь для доступа в онлайнTitle screen
[References: p. 140 (4 tit.)]
In the work composition material has been investigated based on steel Cr20NMn20 deposited for several passes until obtaining the layer 6 mm for steel base 3, of dimensions 120x20 mm and thickness 3 mm at the installation ERI-5. Selection of coating composition is conditioned by prospect of its application as the material possessing high wear-resistant properties under the conditions of abrasive wear and contact friction with high specific loads. Coating structure has been investigated through metallographic microscope of the instrument NANOHARDNESS TESTER. Estimation of thermal processes in the zone of electronic beam in mutual relations with experimental investigation of the structure and phase composition of coating is thus investigated.
Для данного заглавия нет комментариев.