Thermal shock removal of defective glass-enamel coating from cast-iron products / A. D. Aleutdinov [et al.]
Уровень набора: (RuTPU)RU\TPU\network\2008, IOP Conference Series: Materials Science and EngineeringЯзык: английский.Страна: .Резюме или реферат: A setup for light beam exposure has been developed. The setup was used to consider the technology of thermal shock destruction of the coating by pulsed-periodic exposure to powerful focused light from the xenon arc lamp DKsShRB-10000. It is shown that this type of exposure can effectively remove the glass-enamel coating from iron products. The optimal mode of setup operation to efficiently remove the defective glass-enamel coating is found: the diameter of the focused light beams is 2.5-3.5 cm; the lamp arc pulse current is 350-450 A; pulse duration is (0.5-1) s and pulse repetition frequency is (0.15-0.5) s-1..Примечания о наличии в документе библиографии/указателя: [References: 5 tit.].Аудитория: .Тематика: электронный ресурс | труды учёных ТПУ Ресурсы он-лайн:Щелкните здесь для доступа в онлайн | Щелкните здесь для доступа в онлайнНет реальных экземпляров для этой записи
Title screen
[References: 5 tit.]
A setup for light beam exposure has been developed. The setup was used to consider the technology of thermal shock destruction of the coating by pulsed-periodic exposure to powerful focused light from the xenon arc lamp DKsShRB-10000. It is shown that this type of exposure can effectively remove the glass-enamel coating from iron products. The optimal mode of setup operation to efficiently remove the defective glass-enamel coating is found: the diameter of the focused light beams is 2.5-3.5 cm; the lamp arc pulse current is 350-450 A; pulse duration is (0.5-1) s and pulse repetition frequency is (0.15-0.5) s-1.
Adobe Reader
Для данного заглавия нет комментариев.
Личный кабинет оставить комментарий.