Features of pore structure of the products of ac electrochemical oxidation of copper and aluminium / N. V. Usoltseva, V. V. Korobochkin
Язык: английский.Страна: Россия.Серия: Секция 6. Технические наукиРезюме или реферат: Products of the simultaneous AC electrochemical oxidation of copper and aluminum were investigated using X-ray diffraction, scanning electron microscopy and thermal desorptionof nitrogen. The content of copper-species in the samples obtained in sodium chloride solutions increases with the current density of 1 to 2 A/cm2. The products are characterized bya specific surface area of more 200 m2/g, a mesoporous structure and a change of pore sizedistribution with the current density variation. Porous agglomerates of the electrolysis productsbecome smaller with increasing current density of 1 A/cm2(< 15 microns) to 2 A/cm2(<7 microns)..Примечания о наличии в документе библиографии/указателя: [Библиогр.: с. 112 (8 назв.)].Тематика: труды учёных ТПУ | alternating current | electrolysis | metal oxides | LDH | specific surface | pore structure Ресурсы он-лайн:Щелкните здесь для доступа в онлайнНет реальных экземпляров для этой записи
Заглавие с экрана
[Библиогр.: с. 112 (8 назв.)]
Products of the simultaneous AC electrochemical oxidation of copper and aluminum were investigated using X-ray diffraction, scanning electron microscopy and thermal desorptionof nitrogen. The content of copper-species in the samples obtained in sodium chloride solutions increases with the current density of 1 to 2 A/cm2. The products are characterized bya specific surface area of more 200 m2/g, a mesoporous structure and a change of pore sizedistribution with the current density variation. Porous agglomerates of the electrolysis productsbecome smaller with increasing current density of 1 A/cm2(< 15 microns) to 2 A/cm2(<7 microns).
Для данного заглавия нет комментариев.
Личный кабинет оставить комментарий.