Formation of Disordered Dislocational Substructures and Fracture of Cu-Mn Polycrystal Solid Solutions / N. A. Koneva [et al.]
Уровень набора: (RuTPU)RU\TPU\network\4816, AIP Conference ProceedingsЯзык: английский.Резюме или реферат: The evolution of dislocational substructures (DSS) during deformation was investigated using the TEM method. The process was held up to the fracture of Cu-Mn polycrystalline solid solutions with various grain sizes. The interconnection of microcracks formation in the alloys with the dislocation substructures being formed was revealed. It was established that the microcracks are formed along the grain boundaries and the disoriented substructure boundaries. The reasons for different plasticity of alloys with small and large Mn content are discussed..Примечания о наличии в документе библиографии/указателя: [References: 12 tit.].Аудитория: .Тематика: электронный ресурс | труды учёных ТПУ | неупорядоченные структуры | твердые растворы | субструктуры | микротрещины | сплавы | пластичность Ресурсы он-лайн:Щелкните здесь для доступа в онлайнНет реальных экземпляров для этой записи
Title screen
[References: 12 tit.]
The evolution of dislocational substructures (DSS) during deformation was investigated using the TEM method. The process was held up to the fracture of Cu-Mn polycrystalline solid solutions with various grain sizes. The interconnection of microcracks formation in the alloys with the dislocation substructures being formed was revealed. It was established that the microcracks are formed along the grain boundaries and the disoriented substructure boundaries. The reasons for different plasticity of alloys with small and large Mn content are discussed.
Для данного заглавия нет комментариев.
Личный кабинет оставить комментарий.