Positron Annihilation Study of Vacancy-Type Defects in Al Single Crystal Foils with the Tweed Structures Across the Surface / P. V. Kuznetsov [et al.]
Уровень набора: (RuTPU)RU\TPU\network\4816, AIP Conference ProceedingsЯзык: английский.Резюме или реферат: The vacancy-type defects in the aluminum single crystal foils after a series of the cyclic tensions were studied using positron annihilation. Two components were identified in the positron lifetime spectra associated with the annihilation of free positrons and positrons trapped by dislocations. With increasing number of cycles the dislocation density firstly increases and reaches a maximum value at N=10 000 cycles but then it gradually decreases and at N=70 000 cycles falls down to the level typical for the virgin samples. The direct evidence on the formation of a two-phase system "defective near-surface layer/base Al crystal" in aluminum foils at cyclic tension was obtained using a positron beam with the variable energy..Примечания о наличии в документе библиографии/указателя: [References: 16 tit.].Аудитория: .Тематика: электронный ресурс | труды учёных ТПУ | позитроны | вакансии | дефекты | структуры | поверхности | алюминиевые пленки | монокристаллические пленки | аннигиляция | алюминиевая фольга Ресурсы он-лайн:Щелкните здесь для доступа в онлайнTitle screen
[References: 16 tit.]
The vacancy-type defects in the aluminum single crystal foils after a series of the cyclic tensions were studied using positron annihilation. Two components were identified in the positron lifetime spectra associated with the annihilation of free positrons and positrons trapped by dislocations. With increasing number of cycles the dislocation density firstly increases and reaches a maximum value at N=10 000 cycles but then it gradually decreases and at N=70 000 cycles falls down to the level typical for the virgin samples. The direct evidence on the formation of a two-phase system "defective near-surface layer/base Al crystal" in aluminum foils at cyclic tension was obtained using a positron beam with the variable energy.
Для данного заглавия нет комментариев.