Wear Mechanisms of Sintered Self-Lubricating Al-based Composites under Dry Friction / N. M. Rusin, A. L. Skorentsev, A. V. Gurskikh

Уровень набора: (RuTPU)RU\TPU\network\4816, AIP Conference ProceedingsОсновной Автор-лицо: Rusin, N. M.Альтернативный автор-лицо: Skorentsev, A. L., physicist, engineer of Tomsk Polytechnic University, 1987-, Aleksandr Leonidovich;Gurskikh, A. V., specialist in the field of mechanical engineering, Associate Professor of Tomsk Polytechnic University, candidate of technical sciences, 1981-, Aleksey ValerievichКоллективный автор (вторичный): Национальный исследовательский Томский политехнический университет (ТПУ), Физико-технический институт (ФТИ), Кафедра общей физики (ОФ)Язык: английский.Резюме или реферат: The composition and structure of the surface layer, formed as a result of dry friction of the steel disc and Al-Sn composites, were studied. The research showed that the final stage of composites wearing is the destruction of the thin surface layer formed as a result of the sample's material and oxide particles mixing during dry friction..Примечания о наличии в документе библиографии/указателя: [References: 6 tit.].Аудитория: .Тематика: электронный ресурс | труды учёных ТПУ | композиты | сухое трение | поверхностные слои Ресурсы он-лайн:Щелкните здесь для доступа в онлайн
Тэги из этой библиотеки: Нет тэгов из этой библиотеки для этого заглавия. Авторизуйтесь, чтобы добавить теги.
Оценка
    Средний рейтинг: 0.0 (0 голосов)
Нет реальных экземпляров для этой записи

Title screen

[References: 6 tit.]

The composition and structure of the surface layer, formed as a result of dry friction of the steel disc and Al-Sn composites, were studied. The research showed that the final stage of composites wearing is the destruction of the thin surface layer formed as a result of the sample's material and oxide particles mixing during dry friction.

Для данного заглавия нет комментариев.

оставить комментарий.