The morphology, elemental, phase composition, nanohardness, and Young's modulus of the hydroxyapatite (HA) coating deposited via radio frequency (RF) magnetron sputtering onto the AZ31 surface were investigated by atomic force microscopy (AFM), scanning electron microscopy (SEM), energy dispersive X-ray spectroscopy (EDX), X-ray diffraction (XRD), and nanoindentationtechniques. The calcium phosphate (Ca/P) molar ratio of the HA coating deposited via RF-magnetron sputtering onto AZ31 substrates according to EDX was 1.570.03. The SEM experiments revealed significant differences in the morphology of the HA film deposited on untreated and treated with the pulsed electron beam (PEB) AZ31 substrate. Nanoindentation studies demonstrated significant differences in the mechanical responses of the HA film deposited on the initial and PEB-modified AZ31 substrates. The nanoindentation hardness and the Young's modulus of the HA film on the magnesium alloy modified using the PEB treatment were higher than that of the HA layer on the untreated substrate. Moreover, the HA film fabricated onto the PEB-treated surface was more resistant to plastic deformation than the same film on the untreated AZ31 surface.