Regularities of Structure and Phase Composition Formation of Surface Layer of Silumin Subjected to Electron-Beam Treatment / A. V. Tkachenko [et al.]
Уровень набора: (RuTPU)RU\TPU\network\11477, Key Engineering Materials, Scientific JournalЯзык: английский.Серия: Discharge and Plasma-Beam TechnologyРезюме или реферат: It has been shown that electron beam treatment of silumin is accompanied by the formation of multilayer submicro-and nanocrystalline structure and result in increasing the microhardness of the surface layer (towards the core) is ~ 1.5 times up to 2 GPa. Investigation of cross-sections of the samples also showed an increase of microhardness of the surface layers up to 50 [mu]m and 70 [mu]m under the best conditions of irradiation on "GEZA-1" setup and "SOLO" setup respectively..Аудитория: .Тематика: электронный ресурс | труды учёных ТПУ | электронно-лучевая обработка | наноструктуры | силумины | структуры | фазовый состав | поверхностные слои | микротвердость | поверхностные слои Ресурсы он-лайн:Щелкните здесь для доступа в онлайнНет реальных экземпляров для этой записи
Title screen
It has been shown that electron beam treatment of silumin is accompanied by the formation of multilayer submicro-and nanocrystalline structure and result in increasing the microhardness of the surface layer (towards the core) is ~ 1.5 times up to 2 GPa. Investigation of cross-sections of the samples also showed an increase of microhardness of the surface layers up to 50 [mu]m and 70 [mu]m under the best conditions of irradiation on "GEZA-1" setup and "SOLO" setup respectively.
Для данного заглавия нет комментариев.
Личный кабинет оставить комментарий.