Development of bioceramic material for spinal surgery implants / T. Sablina [et al.]
Уровень набора: (RuTPU)RU\TPU\network\2008, IOP Conference Series: Materials Science and EngineeringЯзык: английский.Страна: .Резюме или реферат: Highly porous zirconia-based ceramics were prepared. The ceramic samples sintered at 1600°C had porosities from 40% to 43%, with pore size ranges as follows: "big pore" 100-220 pm and "small pore" 0.8-8 pm. This makes the ceramic structure to be very similar to the structure of the natural spinal bone. The level of mechanical properties of the synthesized zirconia-based ceramics is determined by the pore sizes. The values of the compressive strength and the effective Young's modulus are very similar to those characteristics of the natural spinal bone..Примечания о наличии в документе библиографии/указателя: [References: 11 tit.].Тематика: электронный ресурс | труды учёных ТПУ | биокерамические материалы | имплантанты | диоксид циркония | керамика | модуль Юнга | кости | позвоночник Ресурсы он-лайн:Щелкните здесь для доступа в онлайн | Щелкните здесь для доступа в онлайнНет реальных экземпляров для этой записи
Title screen
[References: 11 tit.]
Highly porous zirconia-based ceramics were prepared. The ceramic samples sintered at 1600°C had porosities from 40% to 43%, with pore size ranges as follows: "big pore" 100-220 pm and "small pore" 0.8-8 pm. This makes the ceramic structure to be very similar to the structure of the natural spinal bone. The level of mechanical properties of the synthesized zirconia-based ceramics is determined by the pore sizes. The values of the compressive strength and the effective Young's modulus are very similar to those characteristics of the natural spinal bone.
Для данного заглавия нет комментариев.
Личный кабинет оставить комментарий.