Microplasma synthesis of biocompatible coatings with additions of magnesium, silicon and silver on pure titanium from homogeneous electrolytes / O. P. Terleeva [et al.]
Уровень набора: Surface and Coatings TechnologyЯзык: английский.Резюме или реферат: The coating was produced by microplasma process (plasma electrolytic oxidation, microarc oxidation) of Ti substrate. The coatings formed in basic solution containing Ca2 +, EDTA4 −, PO43 −, Mg, Si, Ag were selected as additives in the anodizing bath to produce modified Ca/P coatings. The morphology, phase and elemental composition of the coating were characterised using scanning electron microscopy, X-ray diffraction and EDX analysis. The results showed that Mg, Si, Ag additions were successfully incorporated. The coatings mainly consists of anatase, rutile and calcium phosphates and besides Mg incorporated coatings contain additionally CaMg(CO3)2, CaCO3, MgCO3 and Ca9.5Mg0.5P7O28; the Si-incorporated coatings contain additionally CaTiSiO5 phases. The way was found to regulate the characteristics of the coatings by introducing desired elements, such as Mg, Si, Ag by microplasma technique..Примечания о наличии в документе библиографии/указателя: [References: 42 tit.].Аудитория: .Тематика: электронный ресурс | труды учёных ТПУ | биосовместимые покрытия | титан | магний | серебро | дополнения Ресурсы он-лайн:Щелкните здесь для доступа в онлайнTitle screen
[References: 42 tit.]
The coating was produced by microplasma process (plasma electrolytic oxidation, microarc oxidation) of Ti substrate. The coatings formed in basic solution containing Ca2 +, EDTA4 −, PO43 −, Mg, Si, Ag were selected as additives in the anodizing bath to produce modified Ca/P coatings. The morphology, phase and elemental composition of the coating were characterised using scanning electron microscopy, X-ray diffraction and EDX analysis. The results showed that Mg, Si, Ag additions were successfully incorporated. The coatings mainly consists of anatase, rutile and calcium phosphates and besides Mg incorporated coatings contain additionally CaMg(CO3)2, CaCO3, MgCO3 and Ca9.5Mg0.5P7O28; the Si-incorporated coatings contain additionally CaTiSiO5 phases. The way was found to regulate the characteristics of the coatings by introducing desired elements, such as Mg, Si, Ag by microplasma technique.
Для данного заглавия нет комментариев.