Effect of ion irradiation on the surface energy of deposited coatings / E. N. Eremin [et al.]
Уровень набора: (RuTPU)RU\TPU\network\2008, IOP Conference Series: Materials Science and EngineeringЯзык: английский.Серия: Physical and chemical phenomena in inorganic materials in radiation, electrical and thermal fieldsРезюме или реферат: We investigated multi-element coatings exposed to argon ion bombardment. The coatings were irradiated using a multi-ampere hollow-cathode ion source. The arc current was 1 A, and the potential of the substrate was maintained equal to 300 V. The surface tension (surface energy) of the coatings was measured before and after irradiation through the size-dependence of the microhardness and electrical resistivity of coatings on their thickness. Ion irradiation was found to affect the surface energy of the coatings in different ways. This is due to both the structure of the coating and its elemental composition..Примечания о наличии в документе библиографии/указателя: [References: 10 tit.].Тематика: электронный ресурс | труды учёных ТПУ | ионное облучение | поверхностная энергия | покрытия | ионы аргона | микротвердость Ресурсы он-лайн:Щелкните здесь для доступа в онлайн | Щелкните здесь для доступа в онлайнНет реальных экземпляров для этой записи
Title screen
[References: 10 tit.]
We investigated multi-element coatings exposed to argon ion bombardment. The coatings were irradiated using a multi-ampere hollow-cathode ion source. The arc current was 1 A, and the potential of the substrate was maintained equal to 300 V. The surface tension (surface energy) of the coatings was measured before and after irradiation through the size-dependence of the microhardness and electrical resistivity of coatings on their thickness. Ion irradiation was found to affect the surface energy of the coatings in different ways. This is due to both the structure of the coating and its elemental composition.
Для данного заглавия нет комментариев.
Личный кабинет оставить комментарий.