Preparation of NiO-CuO-MgO fine powders by ultrasonic spray pyrolysis for carbon nanofibers synthesis / I. V. Krasnikova [et al.]
Уровень набора: Chemical Physics LettersЯзык: английский.Резюме или реферат: Carbon nanofibers with uniform diameter distribution are of great importance to be applied in composite materials production. Characteristics of the final carbon product obtained via catalytic chemical vapour deposition are known to be determined by the catalyst characteristics and the process conditions. In this work, ultrasonic spray pyrolysis was used for the preparation of uniform-sized NiO-CuO-MgO fine powders. Spherical particles of 170–340 nm in diameter were obtained in a temperature range of 400–600 °C. Synthesized powders exhibited high catalytic activity in CCVD of ethylene with the formation of CNF with relatively narrow diameter distribution (60 ± 20 nm)..Примечания о наличии в документе библиографии/указателя: [References: 19 tit.].Аудитория: .Тематика: электронный ресурс | труды учёных ТПУ | пиролиз | наноразмерные частицы | углеродные нановолокна | химическое осаждение Ресурсы он-лайн:Щелкните здесь для доступа в онлайнTitle screen
[References: 19 tit.]
Carbon nanofibers with uniform diameter distribution are of great importance to be applied in composite materials production. Characteristics of the final carbon product obtained via catalytic chemical vapour deposition are known to be determined by the catalyst characteristics and the process conditions. In this work, ultrasonic spray pyrolysis was used for the preparation of uniform-sized NiO-CuO-MgO fine powders. Spherical particles of 170–340 nm in diameter were obtained in a temperature range of 400–600 °C. Synthesized powders exhibited high catalytic activity in CCVD of ethylene with the formation of CNF with relatively narrow diameter distribution (60 ± 20 nm).
Для данного заглавия нет комментариев.