Corundum Refractory Material in Alumina-Binder Resistant to High-Temperature Deformation / P. M. Pletnev [et al.]
Уровень набора: Refractories and Industrial CeramicsЯзык: английский.Страна: .Резюме или реферат: In order to provide a good resistance for refractory structures towards high-temperature deformation during manufacture of engineering ceramic during firing at 1650°C a corundum refractory material is developed with a weight faction of more than 95 wt.% Al2O3. The ceramic binder used is high-temperature calcium hexa-aluminate formed during firing molded objects from a thixotropic mixture consisting of refractory filler of electromelted corundum and components for forming a binder, i.e., high-alumina cement (HAC) and finely ground alumina..Примечания о наличии в документе библиографии/указателя: [References: p. 90 (16 tit.)].Аудитория: .Тематика: электронный ресурс | труды учёных ТПУ | calcium hexa-aluminate | electromelted corundum | thixotropic mixture | alumina ceramic binder | алюминат кальция | тиксотропные горючие Ресурсы он-лайн:Щелкните здесь для доступа в онлайнНет реальных экземпляров для этой записи
Title screen
[References: p. 90 (16 tit.)]
In order to provide a good resistance for refractory structures towards high-temperature deformation during manufacture of engineering ceramic during firing at 1650°C a corundum refractory material is developed with a weight faction of more than 95 wt.% Al2O3. The ceramic binder used is high-temperature calcium hexa-aluminate formed during firing molded objects from a thixotropic mixture consisting of refractory filler of electromelted corundum and components for forming a binder, i.e., high-alumina cement (HAC) and finely ground alumina.
Для данного заглавия нет комментариев.
Личный кабинет оставить комментарий.