Structural Changes in С36 Laves Phase Intermetallic Compound TiCr2 During Hydrogenation–Dehydrogenation Process / T. L. Murashkina, M. S. Syrtanov, R. S. Laptev
Уровень набора: Russian Physics JournalЯзык: английский.Резюме или реферат: The paper deals with melting of titanium and chromium metal powders in plasma of abnormal glow discharge which results in the formation of the hexagonal С36 Laves phase compound TiCr2 with a = 4.928 A and c = 15.983 A lattice parameters. The hydrogenation–dehydrogenation process is used to prepare the powder of C36 Laves phase intermetallic compound TiCr. The hydrogenation–dehydrogenation process is performed at 100°C, 2 atm hydrogen pressure and 30 min ageing followed by vacuum cooling. The prepared metal powder is characterized by rounded lamellar and coarse particles 6 ± 2 ?m and 21 ± 7 ?m in size, respectively..Примечания о наличии в документе библиографии/указателя: [References: 15 tit.].Аудитория: .Тематика: электронный ресурс | труды учёных ТПУ | intermetallic compound | Laves phase | abnormal glow discharge | X-ray diffraction | hydrogenation | интерметаллидные соединения | фазы Лавеса | тлеющий разряд | рентгеновская дифракция Ресурсы он-лайн:Щелкните здесь для доступа в онлайнНет реальных экземпляров для этой записи
Title screen
[References: 15 tit.]
The paper deals with melting of titanium and chromium metal powders in plasma of abnormal glow discharge which results in the formation of the hexagonal С36 Laves phase compound TiCr2 with a = 4.928 A and c = 15.983 A lattice parameters. The hydrogenation–dehydrogenation process is used to prepare the powder of C36 Laves phase intermetallic compound TiCr. The hydrogenation–dehydrogenation process is performed at 100°C, 2 atm hydrogen pressure and 30 min ageing followed by vacuum cooling. The prepared metal powder is characterized by rounded lamellar and coarse particles 6 ± 2 ?m and 21 ± 7 ?m in size, respectively.
Для данного заглавия нет комментариев.
Личный кабинет оставить комментарий.