Effect of temperature and pressure on mixed oxide solid solutions / M. Yu. Petrushina, E. S. Dedova, K. V. Yusenko [et al.]
Уровень набора: Inorganic Chemistry CommunicationsЯзык: английский.Страна: .Резюме или реферат: A hydrothermal synthesis of ZrW2-xMoxO8 (0 ≤ x ≤ 2) from the corresponding precursors is reported in this paper. High-temperature and high-pressure data are presented for the sample with x = 1.6. An increase in temperature initiates the phase transition from tetragonal precursor to orthorhombic-ZrW2-xMoxO8 (x = 1.6) with the subsequent formation of cubic and trigonal phases. The thermolysis parameter of the disordered cubic ZrW2-xMoxO8 (x = 1.6) phase is 803 K, and the coefficient of thermal expansion is α = -4.6∙10-6 K−1. Data on ZrW2-xMoxO8 (x = 1.6) structure as a function of pressure are obtained for the first time. Pressure-induced changes from cubic to orthorhombic ZrW2-xMoxO8 (x = 1.6) phase at 1.38 GPa are observed. The sample amorphization is irreversible during decompression..Примечания о наличии в документе библиографии/указателя: [References: 27 tit.].Аудитория: .Тематика: электронный ресурс | труды учёных ТПУ | оксиды | твердые растворы Ресурсы он-лайн:Щелкните здесь для доступа в онлайнTitle screen
[References: 27 tit.]
A hydrothermal synthesis of ZrW2-xMoxO8 (0 ≤ x ≤ 2) from the corresponding precursors is reported in this paper. High-temperature and high-pressure data are presented for the sample with x = 1.6. An increase in temperature initiates the phase transition from tetragonal precursor to orthorhombic-ZrW2-xMoxO8 (x = 1.6) with the subsequent formation of cubic and trigonal phases. The thermolysis parameter of the disordered cubic ZrW2-xMoxO8 (x = 1.6) phase is 803 K, and the coefficient of thermal expansion is α = -4.6∙10-6 K−1. Data on ZrW2-xMoxO8 (x = 1.6) structure as a function of pressure are obtained for the first time. Pressure-induced changes from cubic to orthorhombic ZrW2-xMoxO8 (x = 1.6) phase at 1.38 GPa are observed. The sample amorphization is irreversible during decompression.
Для данного заглавия нет комментариев.