Study of tritium and helium generation and release from lead-lithium eutectics Li15.7Pb under neutron irradiation / T. V. Kulsartov, Zh. A. Zaurbekova, I. L. Tazhibaeva [et al.]
Уровень набора: Fusion Engineering and DesignЯзык: английский.Страна: .Резюме или реферат: This paper describes the experiments on study of tritium and helium generation and release processes from lead-lithium eutectics Li15.7Pb. The irradiation was performed at the IVG.1M research reactor at 6 MW of thermal power. The irradiation temperature increased step by step from 225 to 550 °C. A qualitative assessment of the experimental results showed that as the temperature rises above 390 °C, the tritium flux from the sample consisting of T2 and HT molecules decreases. It was concluded that the observed effect is similar to the previously observed one for lead-lithium eutectics with Li17Pb83 composition..Примечания о наличии в документе библиографии/указателя: [References: p. 1320 (16 tit.)].Аудитория: .Тематика: электронный ресурс | труды учёных ТПУ | lead-lithium eutectics | neutron irradiation | tritium | helium | эвтектики | облучение | тритий | гелий | генерация Ресурсы он-лайн:Щелкните здесь для доступа в онлайнНет реальных экземпляров для этой записи
Title screen
[References: p. 1320 (16 tit.)]
This paper describes the experiments on study of tritium and helium generation and release processes from lead-lithium eutectics Li15.7Pb. The irradiation was performed at the IVG.1M research reactor at 6 MW of thermal power. The irradiation temperature increased step by step from 225 to 550 °C. A qualitative assessment of the experimental results showed that as the temperature rises above 390 °C, the tritium flux from the sample consisting of T2 and HT molecules decreases. It was concluded that the observed effect is similar to the previously observed one for lead-lithium eutectics with Li17Pb83 composition.
Для данного заглавия нет комментариев.
Личный кабинет оставить комментарий.