Experimental and theoretical studies helped to reveal patterns of surface roughening and the microstructure refinement in the surface layer of commercial pure titanium during ultrasonic impact treatment. Applying transmission electron microscopy technique, a gradient microstructure in the surface layer of the ultrasonically treated sample, where the grain size is varied from nano- to micrometers was revealed. It was shown that the surface plastic strains of the titanium sample proceeded according to the plastic ploughing mechanism, which was accompanied by dislocation sliding, twinning, and the transformations of the microstructure and phase composition. The molecular dynamics method was applied to demonstrate the mechanism of the phase transformations associated with the formation of stacking faults, as well as the reversible displacement of atoms from their sites in the hcp lattice, causing a change in coordination numbers. The role of the electronic subsystem in the development of the strain-induced phase transformations during ultrasonic impact treatment was discussed.