The effect of counterbody on tribological adaptation of an electron beam deposited HSS M2 steel coating in a range of sliding speeds and normal loads / S. F. Gnyusov, E. A. Fedin, S. Yu. Tarasov
Уровень набора: Tribology InternationalЯзык: английский.Страна: .Резюме или реферат: A relationship between wear behavior and structural-phase state of HSS M2 electron beam cladded coating rubbed against AISI52100 or AISIO7 counterbodies in a range of loads and speeds has been established. When rubbing the coating against the AISIO7 counterbody the wear rate increased with the normal load while coefficient of friction decreased. The effect of the counterbody on wear and friction higher speeds was related to generation of mechanically mixed layers (MMLs) composed of iron tungstate, carbide fragments and transferred metal. Steady wear rate vs. time dependence in M2/AISI O7 pair is due to higher amount of this mixed oxide..Примечания о наличии в документе библиографии/указателя: [References: 39 tit.].Аудитория: .Тематика: электронный ресурс | труды учёных ТПУ | coating | abrasive | wear | third body | покрытия | стали | электронные пучки | трение | износостойкость Ресурсы он-лайн:Щелкните здесь для доступа в онлайнНет реальных экземпляров для этой записи
Title screen
[References: 39 tit.]
A relationship between wear behavior and structural-phase state of HSS M2 electron beam cladded coating rubbed against AISI52100 or AISIO7 counterbodies in a range of loads and speeds has been established. When rubbing the coating against the AISIO7 counterbody the wear rate increased with the normal load while coefficient of friction decreased. The effect of the counterbody on wear and friction higher speeds was related to generation of mechanically mixed layers (MMLs) composed of iron tungstate, carbide fragments and transferred metal. Steady wear rate vs. time dependence in M2/AISI O7 pair is due to higher amount of this mixed oxide.
Для данного заглавия нет комментариев.
Личный кабинет оставить комментарий.