Applicability Boron-Containing Materials Obtained by Self-Propagating High-Temperature Synthesis in Radiation Protection Technology = Обоснование возможности применения борсодержащих материалов, полученных в режиме самораспространяющегося высокотемпературного синтеза, в технике радиационной защиты / O. Yu. Dolmatov, M. S. Kuznetsov, A. O. Semenov [et al.]
Уровень набора: Atomic EnergyЯзык: английский.Страна: .Резюме или реферат: Research on obtaining heavy-metal borides for the radiation protection of non-extended objects by an energy-efficient method of unconventional powder metallurgy – self-propagating high-temperature synthesis – is presented. The protective properties of two materials based on lanthanum hexaboride and tungsten boride were synthesized and investigated. Mechanical activation of the charge was used as a method of controlling self-propagating high-temperature synthesis at the sample preparation stage in order to obtain systems with the specified optimal phase composition. The lanthanum hexaboride and tungsten boride samples obtained with weight content 90 and 85%, respectively, in the course of the experiments were investigated as materials providing shielding against a high-energy neutron flux from a plutonium-beryllium source. It was found on the basis of the experiments that the nuclear-physical properties as well as the mass and size parameters of the obtained materials are suitable for effective protection of non-extended objects from a fast-neutron flux.; В статье представлены исследования в области получения боридов тяжелых металлов для радиационной защиты непротяженных объектов энергетически эффективным методом нетрадиционной порошковой металлургии - самораспространяющимся высокотемпературным синтезом. Проводились синтез и исследование защитных свойств двух материалов на основе гексаборида лантана и борида вольфрама. Для получения систем с указанным оптимальным фазовым составом применялся метод механической активации шихты как способ управления самораспространяющимся высокотемпературным синтезом на стадии подготовки образцов. Полученные в ходе экспериментов образцы гексаборида лантана и борида вольфрама соответственно с массовым содержанием 90 и 85% по массе были исследованы в качестве защитных материалов от потока высокоэнергетичных нейтронов от плутоний-бериллиевого источника. По результатам экспериментов было установлено, что ядерно-физические свойства и массогабаритные параметры полученных материалов позволяют их использовать для эффективной защиты непротяженных объектов от потока быстрых нейтронов.Примечания о наличии в документе библиографии/указателя: [References: 6 tit.].Аудитория: .Тематика: труды учёных ТПУ | электронный ресурс | высокотемпературный синтез | борсодержащие материалы | радиационная защита Ресурсы он-лайн:Щелкните здесь для доступа в онлайнTitle screen
[References: 6 tit.]
Research on obtaining heavy-metal borides for the radiation protection of non-extended objects by an energy-efficient method of unconventional powder metallurgy – self-propagating high-temperature synthesis – is presented. The protective properties of two materials based on lanthanum hexaboride and tungsten boride were synthesized and investigated. Mechanical activation of the charge was used as a method of controlling self-propagating high-temperature synthesis at the sample preparation stage in order to obtain systems with the specified optimal phase composition. The lanthanum hexaboride and tungsten boride samples obtained with weight content 90 and 85%, respectively, in the course of the experiments were investigated as materials providing shielding against a high-energy neutron flux from a plutonium-beryllium source. It was found on the basis of the experiments that the nuclear-physical properties as well as the mass and size parameters of the obtained materials are suitable for effective protection of non-extended objects from a fast-neutron flux.
В статье представлены исследования в области получения боридов тяжелых металлов для радиационной защиты непротяженных объектов энергетически эффективным методом нетрадиционной порошковой металлургии - самораспространяющимся высокотемпературным синтезом. Проводились синтез и исследование защитных свойств двух материалов на основе гексаборида лантана и борида вольфрама. Для получения систем с указанным оптимальным фазовым составом применялся метод механической активации шихты как способ управления самораспространяющимся высокотемпературным синтезом на стадии подготовки образцов. Полученные в ходе экспериментов образцы гексаборида лантана и борида вольфрама соответственно с массовым содержанием 90 и 85% по массе были исследованы в качестве защитных материалов от потока высокоэнергетичных нейтронов от плутоний-бериллиевого источника. По результатам экспериментов было установлено, что ядерно-физические свойства и массогабаритные параметры полученных материалов позволяют их использовать для эффективной защиты непротяженных объектов от потока быстрых нейтронов
Для данного заглавия нет комментариев.