Estimation of A516-70 Carbon Steel Fatigue Damage on the Basis of Acoustic Nonlinearity / A. Lunev [et al.]
Уровень набора: (RuTPU)RU\TPU\network\4816, AIP Conference ProceedingsЯзык: английский.Резюме или реферат: Fatigue damages influence the value of nonlinear acoustic parameter in A516-70 carbon steel was studied. Cyclic loading on a three-point bending scheme was performed. Nonlinear acoustic parameter was measured by the electromagnetic acoustic transducer. It was shown that the maximum of nonlinear acoustic parameter corresponds to the zones with maximum deformation. However, crack growth leads to this value decreasing..Примечания о наличии в документе библиографии/указателя: [References: 13 tit.].Аудитория: .Тематика: электронный ресурс | труды учёных ТПУ | ущербы | усталость | углеродные стали | деформации | трещины | нелинейная акустика | акустический анализ | растрескивание | nonlinear acoustics | acoustic analysis | acoustic transducers | cracking Ресурсы он-лайн:Щелкните здесь для доступа в онлайнНет реальных экземпляров для этой записи
Title screen
[References: 13 tit.]
Fatigue damages influence the value of nonlinear acoustic parameter in A516-70 carbon steel was studied. Cyclic loading on a three-point bending scheme was performed. Nonlinear acoustic parameter was measured by the electromagnetic acoustic transducer. It was shown that the maximum of nonlinear acoustic parameter corresponds to the zones with maximum deformation. However, crack growth leads to this value decreasing.
Для данного заглавия нет комментариев.
Личный кабинет оставить комментарий.