_aFormation of crystalline phases in electroceramics of the system CaO−MgO−Al2O3−SiO2 (A review) _fYu. I. Alekseev, V. I. Vereshchagin |
|
| 320 | _aReferences: p. 343 | ||
| 330 | _aCharacteristics are given for the chemical compounds which are contained in the CaO·Al2O3·2SiO2−CaO·SiO2−MgO·SiO2−SiO2 tetrahedron and constitute the main crystalline phase of a large group of electroceramics. It is shown to be possible to analyze natural magnesia-calcium silicates in a four-component system with allowance for the formation of chemical compounds. The use of diopside raw materials is substantiated and their advantages in the manufacture of electroceramics are assessed | ||
| 333 | _aВ фонде НТБ ТПУ отсутствует | ||
| 390 | _aОригинал на русском языке см.: Стекло и керамика. 1997. N 11. С. 6-9 | ||
| 461 |
_tGlass and Ceramics _d1997 |
||
| 463 |
_tVol. 54, N 11-12 _vP. 340-343 _d1997 |
||
| 610 | 1 | _aтруды учёных ТПУ | |
| 700 | 1 |
_aAlekseev _bYu. I. |
|
| 701 | 1 |
_aVereshchagin _bV. I. _cRussian scientist of chemical engineering _cProfessor of silicates technology of Tomsk Polytechnic University _f1942- _gVladimir Ivanovich _xTPU _2stltpush _3(RuTPU)RU\TPU\pers\26325 |
|
| 801 | 1 |
_aRU _b63413507 _c20100903 |
|
| 801 | 2 |
_aRU _b63413507 _c20120523 _gRCR |
|
| 942 | _cBK | ||