200	1		_aPhase composition, structure and microhardness of tib 2 layers on carbonaceous steels s20 and ша at processing by powerful electron beams in vacuum _fZ. M. Khaltarov [et al.]
203			_aТекст _cэлектронный
300			_aЗаглавие с экрана
320			_a[Библиогр.: 5 назв.]
330			_aWe presented some features of TiB 2 layers crystal structure. Layers were generated on carbonaceous steels S20 and U8A with use reactionary daub containing the titan oxide, a boron and carbon. Layers have been received at pulse and continuous action electron beam processing in vacuum. Properties and a structure of layers depending on a way of formation are compared. Conditions of initiation of process of a self-extending high-temperature synthesis and electron beam surfacing its products are analyzed and compared.
333			_aРежим доступа: по договору с организацией-держателем ресурса
461			_tИзвестия вузов. Физика _oнаучный журнал _fНациональный исследовательский Томский государственный университет (ТГУ) _d1957-
463			_tТ. 55, № 12-2 _v[С. 145-149] _d2012
610	1		_aэлектронный ресурс
610	1		_aтруды учёных ТПУ
610	1		_aэлектронный луч
610	1		_aмикроструктура
701		1	_aKhaltarov _bZ. M.
701		1	_aMilonov _bA. S.
701		1	_aTeresov _bA. D.
701		1	_aKoval _bN. N. _cspecialist in the field of electronics _cProfessor of Tomsk Polytechnic University, Doctor of technical sciences _f1948- _gNikolay Nikolaevich _2stltpush _3(RuTPU)RU\TPU\pers\34748
701		1	_aSemenov _bA. P.
701		1	_aSmirnyagina _bN. N.
712	0	2	_aНациональный исследовательский Томский политехнический университет (ТПУ) _c(2009- ) _2stltpush _3(RuTPU)RU\TPU\col\15902
801		2	_aRU _b63413507 _c20161017 _gRCR
856	4		_uhttp://elibrary.ru/item.asp?id=20133330
942			_cCF