_aCombined plasma and thermal treatment of the Nbc/AISI T1 steel system _fN. N. Cherenda [et al.] |
|
| 203 |
_aText _celectronic |
||
| 300 | _aTitle screen | ||
| 330 | _aCombined plasma and thermal treatment of the NbC/AISI T1 steel system was carried out to improve the strength characteristics of T1 steel. The X-ray diffraction analysis, scanning electron microscopy, energy dispersion microanalysis, and microhardness measurements were used for investigation of the modified layer structure and properties. The findings showed that the treatment of the NbC/T1 steel system by compression plasma flows generated in nitrogen atmosphere led to the dissolution of carbides, formation of ?-NbN nitride, and to a decrease in the steel microhardness. Subsequent annealing in air of a plasma-treated sample for 9 h at a temperature of 600°C resulted in a 1.3 times increase of microhardness compared to the initial steel sample. | ||
| 333 | _aРежим доступа: по договору с организацией-держателем ресурса | ||
| 461 |
_tHigh Temperature Material Processes: An International Quarterly of High-Technology Plasma Processes _d1997- |
||
| 463 |
_tVol. 21, iss. 4 _v[P. 333-343] _d2017 |
||
| 610 | 1 | _aэлектронный ресурс | |
| 610 | 1 | _aтруды учёных ТПУ | |
| 610 | 1 | _aбыстрорежущие стали | |
| 610 | 1 | _aплазма | |
| 610 | 1 | _aотжиг | |
| 610 | 1 | _aкарбиды | |
| 610 | 1 | _aфазовые превращения | |
| 610 | 1 | _aмикротвердость | |
| 701 | 1 |
_aCherenda _bN. N. _cPhysicist _cSenior researcher of Tomsk Polytechnic University, Candidate of physical and mathematical sciences _f1970- _gNikolay Nikolaevich _2stltpush _3(RuTPU)RU\TPU\pers\36741 |
|
| 701 | 1 |
_aUglov _bV. V. _cPhysicist _cLeading researcher of Tomsk Polytechnic University, Doctor of physical and mathematical sciences _f1954- _gVladimir Vasilievich _2stltpush _3(RuTPU)RU\TPU\pers\36737 |
|
| 701 | 1 |
_aKashevsky _bA. M. |
|
| 701 | 1 |
_aAstashinsky _bV. M. _gValentin Mironovich |
|
| 701 | 1 |
_aKuzmitsky _bA. M. _gAnton Mikhaylovich |
|
| 701 | 1 |
_aRemnev _bG. E. _cphysicist _cProfessor of Tomsk Polytechnic University, Doctor of technical sciences _f1948- _gGennady Efimovich _2stltpush _3(RuTPU)RU\TPU\pers\31500 |
|
| 712 | 0 | 2 |
_aНациональный исследовательский Томский политехнический университет _bИсследовательская школа физики высокоэнергетических процессов _c(2017- ) _h8118 _2stltpush _3(RuTPU)RU\TPU\col\23551 |
| 801 | 2 |
_aRU _b63413507 _c20181225 _gRCR |
|
| 856 | 4 | _uhttp://dx.doi.org/10.1615/HighTempMatProc.2018025843 | |
| 942 | _cCF | ||