Nitriding of VT1-0 titanium in low-pressure non-self-maintained glow discharge with the use of different gas mixtures / Y. K. Akhmadeev [et al.]
Уровень набора: Journal of Surface Investigation. X-ray, Synchrotron and Neutron Techniques = 2007-Язык: английский.Резюме или реферат: The results of nitriding of VT1-0 titanium in the plasma of non-self-maintained glow discharge with a hollow cathode are presented. A nitriding process has been implemented in different gas mixtures at low pressure and temperatures less than 650°C. It is shown that two-hour nitriding in a helium-nitrogen mixture leads to formation of a nitrided layer on the specimen’s surface. The obtained layer hardness of 14.5 GPa exceeds the hardness corresponding to pure nitrogen and argon-nitrogen nitriding by a factor of 2 and 1.5, respectively..Примечания о наличии в документе библиографии/указателя: [References: p. 169-170 (11 tit.)].Аудитория: .Тематика: электронный ресурс | труды учёных ТПУ | тлеющий разряд | низкое давление | газовые смеси | азатирование титана Ресурсы он-лайн:Щелкните здесь для доступа в онлайнНет реальных экземпляров для этой записи
Title screen
[References: p. 169-170 (11 tit.)]
The results of nitriding of VT1-0 titanium in the plasma of non-self-maintained glow discharge with a hollow cathode are presented. A nitriding process has been implemented in different gas mixtures at low pressure and temperatures less than 650°C. It is shown that two-hour nitriding in a helium-nitrogen mixture leads to formation of a nitrided layer on the specimen’s surface. The obtained layer hardness of 14.5 GPa exceeds the hardness corresponding to pure nitrogen and argon-nitrogen nitriding by a factor of 2 and 1.5, respectively.
Для данного заглавия нет комментариев.
Личный кабинет оставить комментарий.